Certification: | CE, ISO |
---|---|
Surface: | Smooth Side |
Application: | Transportation Project, Hydraulic Project, Geotechnical Project, Environmental Project |
Feature: | Puncture Resistance, Impact Resistance, Tear Resistance |
Material: | LDPE |
Color: | White |
Lieferanten mit verifizierten Geschäftslizenzen
Nein | Eigenschaften | Testmethode | Testwert | |||||||
1 | Dicke (mm) | ASTM D5199 | 0,50 | 0,75 | 1,00 | 1,25 | 1,50 | 2,00 | 2,50 | 3,00 |
2 | Dichte (g/cm2) | ASTM D1505 | 0,939 | |||||||
3 | Zugfestigkeit (N/mm) | ASTM D6693 | 13 | 20 | 27 | 33 | 40 | 53 | 66 | 80 |
4 | Zugfestigkeit Dehnung % | 800 | ||||||||
5 | 2% des Elastizitätsmoduls N/mm |
ASTM D5323 | 210 | 370 | 420 | 520 | 630 | 840 | 1050 | 1260 |
7 | Reißfestigkeit/N | ASTM D1004 | 50 | 70 | 100 | 120 | 150 | 200 | 250 | 300 |
8 | Durchstichfestigkeit/N | ASTM D4833 | 120 | 190 | 250 | 310 | 370 | 500 | 620 | 750 |
9 | Mehrachsige Zugvariable % | ASTM D5617 | 30 | |||||||
10 | Schwarz, „Carbon“ | |||||||||
Schwarzanteil In % | ASTM D1603 | 2,0-3,0 | ||||||||
Carbon Black Dispersion | ASTM D5596 | 10 9viewing Gebiet sollte in der ersten oder zweiten Klasse fallen, dritte Grad ist nicht mehr als 1 | ||||||||
11 | OIT (Oxidative Induction Time) | |||||||||
Standard-OIT/min | ASTM D3895 | 100 | ||||||||
Hochdruck OIT/min | ASTM D5885 | 400 | ||||||||
12 | Ofenreife bei 85 Grad | |||||||||
Standard-OIT-% nach 90 Tagen beibehalten | ASTM D3895 | 35 | ||||||||
Hochdruck-OIT-% nach 90 Tagen erhalten | ASTM D5885 | 60 |