Application: | for Oil Tank Body, and Pressure Container Body. |
---|---|
Grade: | 5series |
Temper: | O, H111, H112, H32 |
Alloy: | 5083t, 5182t 5454t |
Dicke: | 4 _ 8mm |
Breite: | 1000 _ 2400mm |
Lieferanten mit verifizierten Geschäftslizenzen
Chemischer Aufbau | |||||||||
Legierungsserie | Si | F. E. | Cu | Mangan | Mg | Cr | Zn | Ti | |
5083T | Min. | - | - | - | 0.40 | 4.0 | 0.05 | - | - |
Maximum | 0.40 | 0.40 | 0.10 | 1.0 | 4.90 | 0.25 | 0.25 | 0.15 | |
5182T | Min. | - | - | - | 0.20 | 4.0 | - | - | - |
Maximum | 0.20 | 0.35 | 0.15 | 0.50 | 5.0 | 0.1 | 0.25 | 0.1 | |
5454T | Min. | - | - | - | 0.5 | 2.4 | 0.05 | - | - |
Maximum | 0.25 | 0.40 | 0.10 | 1.0 | 3.0 | 0.20 | 0.25 | 0.20 |
Legierungs-Serie | Stä Rke (mm) | Breite (mm) | Lä Nge (mm) | |
5083T | Min. | 4 | 1000 | 2000 |
Maximum | 8 | 2400 | 12600 | |
5182T | Min. | 4 | 1000 | 2000 |
Maximum | 8 | 2400 | 12600 | |
5454T | Min. | 4 | 1000 | 2000 |
Maximum | 8 | 2400 | 12600 |
Legierungs-Serie | Temperament | Ertrag-Stä Rke RP (Mpa) |
DehnfestigkeitRm (Mpa) | Dehnung A (%) |
5083T | O, H111, H112 |
≥ 125 ≥ 125 |
270-350 ≥ 275 |
≥ 15 ≥ 12 |
5182T | O, H111 | ≥ 110 | 255-315 | ≥ 16 |
5454T | O, H111, H112, H32 |
≥ 85 ≥ 125 ≥ 180 |
215-275 ≥ 220 250-305 |
≥ 17 ≥ 8 ≥ 8 |