Produkttyp: | Draht |
---|---|
Material: | Feni |
Kohlenstoffgehalt: | Low Carbon |
PCD: | 98mm |
ET: | 0 |
Loch: | 0 |
Lieferanten mit verifizierten Geschäftslizenzen
Ni | 28, 5~29, 5 | Fe | Bal. | Co | 16, 8~17, 8 | Si | ≤0, 3 |
Mo | ≤0, 2 | Cu | ≤0, 2 | Cr | ≤0, 2 | Mn | ≤0, 5 |
C | ≤0, 03 | P | ≤0, 02 | S | ≤0, 02 |
Code der Bedingung | Bedingung | Draht | Streifen |
R | Weich | ≤585 | ≤570 |
1/4I | 1/4 Hart | 585~725 | 520~630 |
1/2I | 1/2 Hart | 655~795 | 590~700 |
3/4I | 3/4 Hart | 725~860 | 600~770 |
I | Hart | ≥850 | ≥700 |
Dichte (g/cm3) | 8, 2 |
Elektrischer Widerstand bei 20ºC(Om*mm2/m) | 0, 48 |
Temperaturfaktor des Widerstands (20ºC~100ºC)X10-5/ºC | 3, 7~3, 9 |
Curie Point TC/ ºC | 430 |
Elastizitätsmodul, E/ GPA | 138 |
θ/ºC | α1/10-6ºC-1 | θ/ºC | α1/10-6ºC-1 |
20~60 | 7, 8 | 20~500 | 6, 2 |
20~100 | 6, 4 | 20~550 | 7, 1 |
20~200 | 5, 9 | 20~600 | 7, 8 |
20~300 | 5, 3 | 20~700 | 9, 2 |
20~400 | 5, 1 | 20~800 | 10, 2 |
20~450 | 5, 3 | 20~900 | 11, 4 |
θ/ºC | 100 | 200 | 300 | 400 | 500 |
λ/ W/(m*ºC) | 20, 6 | 21, 5 | 22, 7 | 23, 7 | 25, 4 |
Der Wärmebehandlungsprozess | |
Glühen zur Stressabbau | Auf 470~540ºC erhitzt und 1~2 h. Gehalten Kalt |
Glühen | Im Vakuum auf 750~900ºC erhitzt |
Haltezeit | 14 min~1h. |
Abkühlrate | Nicht mehr als 10 ºC/min gekühlt auf 200 ºC |
Name Der Legierungen | Typ | Abmessungen | ||
UALLOY-4J29 | Draht | D = 0, 1~8mm | ||
UALLOY-4J29 | Streifen | W = 5~250mm | T = 0, 1mm | |
UALLOY-4J29 | Folie | W = 10~100mm | T = 0, 01~0, 1 | |
UALLOY-4J29 | Bar | Durchm. = 8~100mm | L= 50~1000 |